鋼纖維材料-鋼纖維混凝土-鋼纖維多少錢(qián)一公斤
鋼纖維混凝土的鋼纖維是一種新型的材料,可以提高混凝土各項(xiàng)強(qiáng)度指標(biāo),一般用于橋梁伸縮縫 隧道伸縮縫 工業(yè)地坪 高速公路修補(bǔ)用。
Steel fiber reinforced concrete in the steel fiber is a new type of material, can improve the concrete strength index, commonly used in bridge expansion joint expansion joint industrial floor highway tunnel repair.
鋼纖維混凝土是在普通混凝土中摻入亂向分布的短鋼纖維所形成的一種新型的多相復(fù)合材料。這些亂向分布的鋼纖維能夠有效地阻礙混凝土內(nèi)部微裂縫的擴(kuò)展及宏觀裂縫的形成，顯著地改善了混凝土的抗拉、抗彎、抗沖擊及抗疲勞性能，具有較好的延性。
Steel fiber reinforced concrete is mixed in ordinary concrete to the distribution of the short steel fiber formed by a new type of multiphase composite materials. These disorderly to the distribution of steel fiber can effectively prevent the expansion of the internal micro cracks of concrete and the formation of macroscopic fracture, noticeably improve the concrete tensile, bending, impact and fatigue resistance, good ductility.
鋼纖維混凝土配合比
鋼纖維混凝土中的鋼纖維體積一般在015%～2%內(nèi)選擇,水灰比不大于015。稠度參考普通混凝土確定。yfkj01
1、地坪一般工程配合比:鋼纖維1%～112%;砂率40%;水灰比0145;塌落度3～5cm。單位用量(kg/m3):鋼纖維78;水泥
400;礫石1233;中砂819;水180。
2、地坪重要工程配合比:鋼纖維115%～118%;砂率46%;水灰比0145;塌落度3～5cm。單位用量(kg/m3):鋼纖維120;水泥450;礫石1210;中砂1035;水200。113鋼纖維混凝土攪拌 鋼纖維混凝土攪拌一般采用強(qiáng)制式攪拌機(jī)攪拌,攪拌時(shí)間為5min。攪拌方法一是將鋼纖維及粗骨料投入攪拌機(jī)攪拌30s,使鋼纖維分散在石子中,再將砂及水泥投入攪拌機(jī)干攪拌30s,注水再攪拌3min左右。這種方法易于操作,攪拌出來(lái)的混凝土中鋼纖維分布較均勻。但鋼纖維及粗骨料先干拌噪音大,易磨損攪拌機(jī)筒體。我們探索出另一種攪拌方法,即在次投鋼纖維及粗骨料時(shí),加入一半量的砂,另一半砂在第二次投料時(shí)再和水泥一起投入攪拌機(jī)。這樣,既達(dá)到降低攪拌噪音,減少筒體磨損的目的,又了攪拌出來(lái)的混凝土中鋼纖維分布均勻。